Analisis Pengaruh Variasi Jumlah Kawat Baja Terhadap Sifat Mekanik dan Struktur Mikro Komposit Aluminium Dengan Proses Sand Casting

Feridiansyah, Dinda Achmad (2025) Analisis Pengaruh Variasi Jumlah Kawat Baja Terhadap Sifat Mekanik dan Struktur Mikro Komposit Aluminium Dengan Proses Sand Casting. Bachelor thesis, Institut Teknologi Kalimantan.

	Text 03191025_cover.pdf Restricted to Repository staff only until 4 January 2027. Download (217kB) | Request a copy
	Text 03191025_statement_of_authenticity.pdf Restricted to Repository staff only until 4 January 2027. Download (2MB) | Request a copy
	Text 03191025_publishing_agreement.pdf Restricted to Repository staff only until 4 January 2027. Download (348kB) | Request a copy
	Text 03191025_approval_sheet.pdf Restricted to Repository staff only until 4 January 2027. Download (3MB) | Request a copy
	Text 03191025_preface.pdf Restricted to Repository staff only until 4 January 2027. Download (6MB) | Request a copy
	Text 03191025_abstract_id.pdf Restricted to Repository staff only until 4 January 2027. Download (304kB) | Request a copy
	Text 03191025_abstract_en.pdf Restricted to Repository staff only until 4 January 2027. Download (404kB) | Request a copy
	Text 03191025_table_of_content.pdf Restricted to Repository staff only until 4 January 2027. Download (420kB) | Request a copy
	Text 03191025_illustrations.pdf Restricted to Repository staff only until 4 January 2027. Download (373kB) | Request a copy
	Text 03191025_tables.pdf Restricted to Repository staff only until 4 January 2027. Download (307kB) | Request a copy
	Text 03191025_notations.pdf Restricted to Repository staff only until 4 January 2027. Download (328kB) | Request a copy
	Text 03191025_chapter_1.pdf Restricted to Repository staff only until 4 January 2027. Download (422kB) | Request a copy
	Text 03191025_chapter_2.pdf Restricted to Repository staff only until 4 January 2027. Download (542kB) | Request a copy
	Text 03191025_chapter_3.pdf Restricted to Repository staff only until 4 January 2027. Download (962kB) | Request a copy
	Text 03191025_chapter_4.pdf Restricted to Repository staff only until 4 January 2027. Download (913kB) | Request a copy
	Text 03191025_conclutions.pdf Restricted to Repository staff only until 4 January 2027. Download (407kB) | Request a copy
	Text 03191025_bibliography.pdf Restricted to Repository staff only until 4 January 2027. Download (365kB) | Request a copy
	Text 03191025_enclosure.pdf Restricted to Repository staff only until 4 January 2027. Download (615kB) | Request a copy
	Text 03191025_paper.pdf Restricted to Repository staff only until 4 January 2027. Download (609kB) | Request a copy
	Text 03191025_presentation.pdf Restricted to Repository staff only until 4 January 2027. Download (1MB) | Request a copy
	Text 03191025_Form. TA-020.pdf Restricted to Repository staff only until 4 January 2027. Download (2MB) | Request a copy

Abstract

Dalam pengecoran logam menggunakan cetakan pasir kualitas produk cor merupakan hal yang sangat penting untuk diperhatikan. Misalnya meningkatkan kualitas sifat mekanik dari hasil cor yang diakibatkan oleh belum adanya penambahan kawat baja di dalam spesimen itu. Penelitian ini menggunakan bahan aluminium bekas yang dilebur kembali. Variasi jumlah kawat baja yang digunakan 0, 1, 2, 3 dan 4 dengan menggunakan metode cetakan pasir. Kekuatan mekanis hasil produk dipengaruhi oleh jumlah penambahan kawat baja pada hasil coran. Tujuan dilakukannya penelitian ini adalah untuk menganalisis sifat mekanik dan struktur mikro terhadap hasil cetak produk. Setelah dilakukan pengujian uji tekan pada spesimen uji didapatkan hasil nilai rata-rata kekuatan tekan tertinggi yaitu pada variasi 2 kawat yaitu 209.06 MPa dan nilai rata-rata kekuatan terendah yaitu pada variasi 4 kawat yaitu sebesar 198.84 MPa, hal ini disebabkan karena cairan aluminium terhambat oleh penambahan kawat yang berada pada tengah spesimen, sehingga mengakibatkan banyaknya udara yang terjebak dan mengakibatkan porositas dan pada hasil pengamatan struktur mikro dengan perbesaran 10x didapatkan ukuran panjang rata-rata batas butir yang paling kecil yaitu pada variasi 4 kawat yaitu sebesar 182.8973 µm, semakin banyaknya kawat yang ditambahkan hal ini juga mengakibatkan banyaknya terjadi porositas pada spesimen uji dan menghasilkan batas butir yang kecil hal ini terjadi karena semakin cepat juga pendinginan pada spesimen uji.

Item Type:	Thesis (Bachelor)
Subjects:	T Technology > TS Manufactures
Divisions:	Jurusan Teknologi Industri dan Proses > Teknik Mesin
Depositing User:	Dinda Achmad Feridiansyah
Date Deposited:	10 Jul 2025 06:32
Last Modified:	10 Jul 2025 06:32
URI:	http://repository.itk.ac.id/id/eprint/23655

Actions (login required)

View Item